Exceed™ 2012 Series are ethylene 1-hexene copolymer resins. Films made from these resins have outstanding toughness, impact strength and puncture. These superior strength properties, along with excellent heat sealing and hot tack performance, make this a very versatile packaging film resin. TnPP is not intentionally added to Exceed™ 2012 resin.
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂加工助剂 | |||
| 成型方式 | 薄膜挤出吹膜吹灌封(BFS) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.912 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 96 °C | Internal | |
熔融温度(Tm) | 114 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 21 % | ASTM D1003 | |
光泽度 | 33 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6.3 Mpa | ASTM D 882 | MD |
屈服(yld) | 6 Mpa | ASTM D 882 | TD |
断裂(brk) | 70 Mpa | ASTM D 882 | MD |
断裂(brk) | 60 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 560 % | ASTM D 882 | MD |
断裂(brk) | 610 % | ASTM D 882 | TD |
穿透强度 | 57 N | Internal | |
耐穿透性 | 5.3 J | Internal | |
埃尔曼多夫撕裂 | 240 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 300 g | ASTM D 1922 | TD |
割线模量 | 100 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 100 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 690 g | ASTM D 1709 |