Exact™ 5101 plastomer resin is an ethylene 1-octene copolymer produced using a proprietary metallocene Technology. Exact™ 5101 is designed for use in both monolayer and multilayer blown film applications requiring outstanding sealing performance and toughness.
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 薄膜挤出吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 94 °C | Internal | |
熔融温度(Tm) | 80 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 2.2 % | ASTM D1003 | |
光泽度 | 82 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 4.7 Mpa | ASTM D 882 | MD |
屈服(yld) | 3.8 Mpa | ASTM D 882 | TD |
断裂(brk) | 60 Mpa | ASTM D 882 | MD |
断裂(brk) | 60 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 420 % | ASTM D 882 | MD |
断裂(brk) | 680 % | ASTM D 882 | TD |
穿透强度 | 54 N | Internal | |
耐穿透性 | 5.4 J | Internal | |
埃尔曼多夫撕裂 | 80 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 310 g | ASTM D 1922 | TD |
割线模量 | 55 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 62 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 380 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。