Exact™ 3237 is an ethylene 1-hexene plastomer designed for use in both monolayer and multilayer film applications. Films made from Exact™ 3237 have a much lower seal initiation temperature than the density suggests along with high toughness, high stiffness, and low COF on hot metal surfaces. The overall combination of properties contributes to enhanced packaging line speeds. TnPP is not intentionally added to Exact™ 3237.
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂加工助剂增滑剂开口剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 薄膜挤出吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.908 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 90 °C | Internal | |
熔融温度(Tm) | 114 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 18 % | ASTM D1003 | |
光泽度 | 35 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 5.9 Mpa | ASTM D 882 | MD |
屈服(yld) | 5.4 Mpa | ASTM D 882 | TD |
断裂(brk) | 60 Mpa | ASTM D 882 | MD |
断裂(brk) | 60 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 480 % | ASTM D 882 | MD |
断裂(brk) | 570 % | ASTM D 882 | TD |
穿透强度 | 57 N | Internal | |
耐穿透性 | 6.3 J | Internal | |
埃尔曼多夫撕裂 | 210 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 280 g | ASTM D 1922 | TD |
割线模量 | 87 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 90 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 800 g | ASTM D 1709 |