UL 04533EH2 is a copolymer of ethylene and vinyl acetate.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Additive | Heat StabilizerFree Flowing Agent | |||
| Appearance | Pellets/Granules | |||
| Processing | Compounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | Internal | |
Vinyl Acetate | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5.0 mm/min |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | 500 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 500 mm/min |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ASTM D 2240 | 15 sec |
Shore D hardness | *** D | ASTM D 2240 | 15 sec |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Melt Temperature(Tm) | *** °C | Internal | Peak |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.