A high crystallinity, high impact copolymer resin designed for injection molded applications requiring excellent processing attributes.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Good StiffnessGood Impact ResistanceGood Heat AgingEasy processingNucleated | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | InjectionCompounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 51 mm/min |
Yield | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Yield | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 1.3 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 13 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
-18℃ (0℉) | *** J/m | ASTM D 256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Falling Dart Impact | *** J | ASTM D 5420 | -29°C, 3.18 mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.