SURLYN™ 9910 is an ionomer of ethylene acid copolymer.
This polymeric material can be processed in conventional extrusion and injection equipment designed to process polyethylene and ethylene copolymer type resins, to create various shapes and sheeting.
Composition
Zinc Ionomer
Applications
Injection Molding / Sheet Extrusion / Blow Molding
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 注塑挤出 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.97 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.7 g/10min | ASTM D1238 | |
磨耗 | 610 - | ASTM D1630 | NBS Index |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 13.8 Mpa | ASTM D638 | |
断裂(brk) | 24.8 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 290 % | ASTM D638 | |
弯曲模量 | 731 Mpa | ASTM D790 | -20 °C |
弯曲模量 | 330 Mpa | ASTM D790 | 23 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 363 J/m | ASTM D256 | |
拉伸冲击 | 1010 kJ/m² | ASTM D 1822 | -40 °C |
拉伸冲击 | 1020 kJ/m² | ASTM D 1822 | 23 °C |
脆化温度 | -105 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 64 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 62 °C | ASTM D1525 | |
熔融温度(Tm) | 86 °C | ASTM D3418 | DSC |
结晶温度 | 46 °C | ASTM D 3418 | DSC |
加工温度 | 185~285 °C | - | |
加工温度 | 285 °C | - | Maximum Processing Temperature |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 6 % | ASTM D1003 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。