ENGAGE™ PV 8660 Polyolefin Elastomer is an ethylene-octene copolymer that offers excellent performance in photovoltaic module encapsulant applications.
ENGAGE™ PV 8660 provides high transmittance, excellent electrical properties, and exceptional anti-damp heat aging, anti-UV aging, and weather resistance properties.
Main Characteristics:
Pellet form
High volume resistivity
High transmittance
Low water vapor transmission rate
Exceptional anti-damp heat aging, anti-UV aging, and weather resistance when cured
Applications:
Photovoltaic module encapsulant
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 耐热老化透光抗紫外线耐候性 | |||
| 颜色形状 | 粒状 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.872 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 4.8 g/10min | ASTM D1238 | |
粘度 | 8 MU | ASTM D1646 | Mooney Viscosity (ML 1+4, 250°F (121°C)) |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 5.7 Mpa | ASTM D638 | 510 mm/min, Compression Molded |
拉伸延伸率 | |||
断裂(brk) | 1100 % | ASTM D638 | 510 mm/min, Compression Molded |
弯曲模量 | 10.9 Mpa | ASTM D790 | 1% Secant : Compression Molded |
弯曲模量 | 10.8 Mpa | ASTM D790 | 2% Secant : Compression Molded |
拉伸模量 | 2.3 Mpa | ASTM D638 | 100% Secant, 510 mm/min, Compression Molded |
撕裂强度 | 37.1 kN/m | ASTM D 624 | Die C |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 66 A | ASTM D 2240 | 1 sec, Compression Molded |
邵氏硬度 D | 17 D | ASTM D 2240 | 1 sec, Compression Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 37 °C | ASTM D1525 | |
熔融温度(Tm) | 72 °C | Internal | DSC, 10°C/min |
玻璃化温度(Tg) | -53 °C | Internal | |
结晶温度 | 44 °C | Internal | DSC |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | Internal |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。