ENGAGE™ 7367 Polyolefin Elastomer is an ethylene-butene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications This product is delivered with a nominal talc partitioning agent to assist in material handling.
Main Characteristics
Pellet form
Excellent flow characteristics
Peroxide, silane, and radiation curable
Improved impact in polypropylene and
polyethylene
High filler loading
Applications
General purpose thermoplastic elastomers
Impact modification
Wire and cable
| Original Document | Technical Datasheet-ASTM(English) | |||
| Appearance | Pellets/Granules | |||
| Processing | Compounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 100% Secant |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | 510 mm/min, Compression Molded |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 510 mm/min, Compression Molded |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 510 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 510 mm/min |
Tear Strength | *** kN/m | ASTM D 624 | Die C |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ASTM D 2240 | |
Shore D hardness | *** D | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Melt Temperature(Tm) | *** °C | Internal | DSC, 10°C/min |
Glass Transition Temperature | *** °C | Internal | |
Freezing temperature | *** °C | Internal | DSC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.