ELITE™ AT 6501 Enhanced Polyethylene Resin is an enhanced LLDPE ethylene-octene copolymer from Dow. It offers a unique combination of low seal initiation temperature, high hot tack strength, high impact resistance, good optical properties and it is easy to process.
Main Characteristics:
Low seal initiation temperature and broad hot tack window
High hot tack strength
Extremely high impact resistance and good tear properties
Good optical properties
High throughput resin with excellent bubble stability
Complies with:
U.S. FDA FCN 424
EU, No 10/2011
Consult the regulations for complete details.
| 原厂资料 | 物性表-ASTM(英文) | |||
| 成型方式 | 薄膜挤出 | |||
| 法规认证 | EU 2011/10/EC (欧盟食品级)FDA(食品药品监督管理局) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.914 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.85 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 102 °C | ASTM D1525 | |
熔融温度(Tm) | 115 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 8.1 % | ASTM D1003 | |
光泽度 | 64 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 9.3 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.2 Mpa | ASTM D 882 | TD |
断裂(brk) | 44 Mpa | ASTM D 882 | MD |
断裂(brk) | 42 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 550 % | ASTM D 882 | MD |
断裂(brk) | 600 % | ASTM D 882 | TD |
穿透强度 | 100 N | Internal | 50 µm |
耐穿透性 | 24 J/cm³ | Internal | 50 µm |
耐穿透性 | 9.6 J | Internal | 50 µm |
埃尔曼多夫撕裂 | 590 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 1000 g | ASTM D 1922 | TD |
割线模量 | 148 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 161 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 1500 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。