ELITE™ AT 6101 Enhanced Polyethylene Resin is a copolymer produced via INSITE™ technology from Dow. It is designed for stretch hooder application and offers a unique combination of holding force, elastic recovery, optics and toughness.
Main Characteristics:
Excellent elastic recovery and holding force
Very high impact resistance and tear properties
Ease of processing
Complies with:
U.S. FDA 21 CFR 175.105(c)(5)
EU, 10/2011
JHOSPA (Japan Hygienic Olefin and Styrene Plastics Association)
Consult the regulations for complete details.
| 原厂资料 | 物性表-ASTM(英文) | |||
| 成型方式 | 吹膜 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ASTM D792 | |
密度 | 0.905 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.8 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 95 °C | ASTM D1525 | |
熔融温度(Tm) | 101 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 4 % | ASTM D1003 | |
光泽度 | 75 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 5.86 Mpa | ASTM D 882 | MD |
屈服(yld) | 5.52 Mpa | ASTM D 882 | TD |
断裂(brk) | 44.8 Mpa | ASTM D 882 | MD |
断裂(brk) | 37.9 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 390 % | ASTM D 882 | MD |
断裂(brk) | 500 % | ASTM D 882 | TD |
穿透强度 | 57.8 N | Internal | 25 µm |
耐穿透性 | 29 J/cm³ | Internal | 25 µm |
耐穿透性 | 5.65 J | Internal | 25 µm |
抗拉韧性 | 66.2 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 70.3 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 200 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 360 g | ASTM D 1922 | TD |
割线模量 | 88.3 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 89.6 Mpa | ASTM D 882 | 1% Secant, TD |
割线模量 | 82.7 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 82.7 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 800 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。