ELITE™ 5401G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking for excellent performance on automated packaging equipment.
For food and specialty packaging films
Superior impact resistance and tear properties
Complies with:
U.S. FDA FCN 424
Canadian HPFB No Objection
EU, No 10/2011
Consult the regulations for complete details.
| 原厂资料 | 物性表-ASTM(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 成型方式 | 吹膜 | |||
| 法规认证 | EU 2011/10/EC (欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D792 | |
密度 | 0.917 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 100 °C | ASTM D1525 | |
熔融温度(Tm) | 123 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 22 % | ASTM D1003 | |
光泽度 | 33 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11.7 Mpa | ASTM D 882 | MD |
屈服(yld) | 11 Mpa | ASTM D 882 | TD |
断裂(brk) | 33.8 Mpa | ASTM D 882 | MD |
断裂(brk) | 27.6 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 400 % | ASTM D 882 | MD |
断裂(brk) | 450 % | ASTM D 882 | TD |
穿透强度 | 35.6 N | Internal | 25 µm |
耐穿透性 | 9.1 J/cm³ | Internal | 25 µm |
耐穿透性 | 1.69 J | Internal | 25 µm |
抗拉韧性 | 70.3 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 66.2 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 250 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 550 g | ASTM D 1922 | TD |
割线模量 | 179 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 200 Mpa | ASTM D 882 | 1% Secant, TD |
割线模量 | 159 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 165 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 450 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。