ELITE™ 5230GC Enhanced Polyethylene Resin is produced via INSITE™ Technology from Dow. Film made from this resin offers high impact strength and good puncture resistance at moderate stretch levels for irregularly shaped loads. In addition, this resin provides excellent extensibility for higher yields on regular loads.
Main Characteristics:
Excellent extensibility
High impact and puncture resistance
Complies with:
U.S. FDA FCN 424
Canadian HPFB No Objection
EU, No 10/2011
Consult the regulations for complete details
| Original Document | Technical Datasheet(English) | |||
| Processing | Cast Film | |||
| Compliance | EU 2011/10/ECFDAHPFB (Canada) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | Internal | DSC |
Processing Temperature | *** °C | - | Melt Temperature |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | 20.3 µm |
Gloss | *** - | ASTM D 2457 | 45°, 20.3 µm |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | MD, 20 µm |
Yield | *** Mpa | ASTM D 882 | TD, 20 µm |
Break | *** Mpa | ASTM D 882 | MD, 20 µm |
Break | *** Mpa | ASTM D 882 | TD, 20 µm |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD, 20 µm |
Break | *** % | ASTM D 882 | TD, 20 µm |
Piercing strength | *** N | Internal | 20 µm |
Puncture resistance | *** J/cm³ | Internal | 20 µm |
Elmondorf Tear | *** g | ASTM D 1922 | MD, 20 µm |
Elmondorf Tear | *** g | ASTM D 1922 | TD, 20 µm |
Dart Drop Impact | *** g | ASTM D 1709 | 20 µm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.