APTIV® 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.
APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.
APTIV 1000 has a unique combination of properties providing high temperature performance, lightweight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen-free and ease of processing makes APTIV films a technology enabler for our customers and end users.
Availability
The films are available in thicknesses from 8 microns up to 750 microns.
| Original Document | Technical Datasheet(English) | |||
| Features | DurabilityHeat ResistanceFlame RetardantHalogen FreeInsulatingWear/Abrasion ResistanceLow Friction/WearEasy processingNon(Low)ToxicChemical ResistanceHydrolysis ResistanceLow Moisture AbsorptionHigh Barrier property/Low permeation | |||
| Appearance | Film | |||
| Compliance | 3A Sanitary StandardsEU 2011/10/ECFDARoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 1000-050G |
Mold Shrinkage | |||
Flow | *** % | Internal | 1000-050G |
Across Flow | *** % | Internal | 1000-050G |
Water Absorption | *** % | ISO 62 | 50% RH, 1000-050G |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM D 696 | 1000-050G |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | 23ºC, 100V |
Dielectric Constant(Permittivity) | |||
10MHz | *** - | ASTM D150 | 23ºC |
Dissipation Factor | |||
10MHz | *** E-4 | ASTM D150 | 23ºC |
Dielectric Strength | *** kV/mm | ASTM D149 | 125µm |
Dielectric Strength | *** kV/mm | ASTM D149 | 250µm |
Dielectric Strength | *** kV/mm | ASTM D149 | 25µm |
Dielectric Strength | *** kV/mm | ASTM D149 | 50µm |
Dielectric Strength | *** kV/mm | ASTM D149 | 6.35mm |
Breakdown Voltage | *** V | ASTM D149 | 125µm |
Breakdown Voltage | *** V | ASTM D149 | 250µm |
Breakdown Voltage | *** V | ASTM D149 | 25µm |
Breakdown Voltage | *** V | ASTM D149 | 50µm |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527-3 | 125µm, MD |
Break | *** Mpa | ISO 527-3 | 125µm, TD |
Break | *** Mpa | ISO 527-3 | 250µm, MD |
Break | *** Mpa | ISO 527-3 | 250µm, TD |
Break | *** Mpa | ISO 527-3 | 25µm, MD |
Break | *** Mpa | ISO 527-3 | 25µm, TD |
Break | *** Mpa | ISO 527-3 | 50µm, MD |
Break | *** Mpa | ISO 527-3 | 50µm, TD |
Break | *** Mpa | ISO 527-3 | MD, 1000-050G |
Break | *** Mpa | ISO 527-3 | TD, 1000-050G |
Tensile Elongation | |||
Break | *** % | ISO 527-3 | 125µm, MD |
Break | *** % | ISO 527-3 | 125µm, TD |
Break | *** % | ISO 527-3 | 250µm, MD |
Break | *** % | ISO 527-3 | 250µm, TD |
Break | *** % | ISO 527-3 | 25µm, MD |
Break | *** % | ISO 527-3 | 25µm, TD |
Break | *** % | ISO 527-3 | 50µm, MD |
Break | *** % | ISO 527-3 | 50µm, TD |
Break | *** % | ISO 527-3 | MD, 1000-050G |
Break | *** % | ISO 527-3 | TD, 1000-050G |
Tensile Modulus | *** Mpa | ISO 527-3 | 125µm, MD |
Tensile Modulus | *** Mpa | ISO 527-3 | 125µm, TD |
Tensile Modulus | *** Mpa | ISO 527-3 | 250µm, MD |
Tensile Modulus | *** Mpa | ISO 527-3 | 250µm, TD |
Tensile Modulus | *** Mpa | ISO 527-3 | 25µm, MD |
Tensile Modulus | *** Mpa | ISO 527-3 | 25µm, TD |
Tensile Modulus | *** Mpa | ISO 527-3 | 50µm, MD |
Tensile Modulus | *** Mpa | ISO 527-3 | 50µm, TD |
Tensile Modulus | *** Mpa | ISO 527-3 | MD, 1000-050G |
Tensile Modulus | *** Mpa | ISO 527-3 | TD, 1000-050G |
Piercing strength | *** kJ/m² | Internal | 1000-050G |
Trouser Tear | *** kN/m | ISO 6383-1 | MD, 1000-050G |
Trouser Tear | *** kN/m | ISO 6383-1 | TD, 1000-050G |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.