High performance Food Grade thermoplastic material, filled PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, colour black. Food Contact compliance for FDA. Drinking water compliance to WRAS (UK).
Typical Application Areas
The VICTREX FG™ 300 family of materials is intended for applications needing wear and abrasion resistance for bearing and wear service and low coefficient of thermal expansion for metal replacement. Chemically resistant to aggressive environments, suitable for sterilisation for food contact applications.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Wear/Abrasion ResistanceLow Friction/WearLow CLTEFood ContactDrinking Water ContactChemical ResistanceFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | InjectionExtrusion | |||
| Compliance | FDAWRAS | |||
| Reinforced | Filler | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Crystalline |
Mold Shrinkage | |||
Flow | % | ISO 294-4 | 390°C nozzle, 200°C tool |
Across Flow | *** % | ISO 294-4 | 390°C nozzle, 200°C tool |
Water Absorption | *** % | ISO 62-1 | Saturation, 100°C, by immersion |
Water Absorption | *** % | ISO 62-1 | Saturation, 23°C, by immersion |
Abrasion resistance | *** mg/1000cy | Internal | CS-17, 1kg |
Spiral Flow | *** mm | - | 390°C nozzle, 200°C tool, 1mm thick |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 125°C |
Break | *** Mpa | ISO 527 | 175°C |
Break | *** Mpa | ISO 527 | 225°C |
Break | *** Mpa | ISO 527 | 23°C |
Break | *** Mpa | ISO 527 | 275°C |
Tensile Elongation | |||
Break | *** % | ISO 527 | 23°C |
Flexural Modulus | *** Mpa | ISO 178 | 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 125°C |
- | *** Mpa | ISO 178 | 175°C |
- | *** Mpa | ISO 178 | 23°C |
- | *** Mpa | ISO 178 | 275°C |
Coefficient of Friction | *** - | ASTM G176 | Block-on-Ring, 10 MPa, 1 m/s |
Coefficient of Friction | *** - | ASTM G176 | Block-on-Ring, 2 MPa, 1 m/s |
Wear Factor | *** E-6 mm³/Nm | ASTM G176 | Block-on-Ring, 10 MPa, 1 m/s |
Wear Factor | *** E-6 mm³/Nm | ASTM G176 | Block-on-Ring, 2 MPa, 1 m/s |
Compressive Strength | *** Mpa | ISO 604 | 120°C |
Compressive Strength | *** Mpa | ISO 604 | 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/U | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | 23°C |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359 | Along flow below Tg |
Flow | *** E-6/K | ISO 11359 | Along flow below Tg |
Across Flow | *** E-6/K | ISO 11359 | Average below Tg |
Across Flow | *** E-6/K | ISO 11359 | Average below Tg |
Melt Temperature(Tm) | *** °C | ISO 11357 | below Tg |
Glass Transition Temperature | *** °C | ISO 11357 | Midpoint |
Glass Transition Temperature | *** °C | ISO 11357 | Onset |
Thermal Conductivity | *** W/(m K) | ISO 22007-4 | Average, 23°C |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | 23°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.