High performance thermoplastic material, unreinforced PolyEtherKetone (PEK), semi crystalline, depth filtered granules for injection moulding, low flow, FDA food contact compliant, colour natural/beige.
Typical Application Areas:
Applications for high strength and stiffness as well as good ductility at higher temperatures. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications.
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 食品接触级医疗级耐化学性高粘度 | |||
| 颜色形状 | 粒状本色米色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | *** g/cm³ | ISO 1183 | Crystalline |
收缩率 | |||
纵向(Flow) | *** % | ISO 294-4 | Along flow |
横向(Across Flow) | *** % | ISO 294-4 | Across flow |
吸水率 | *** % | ISO 62-1 | Saturation, 100°C, by immersion |
吸水率 | *** % | ISO 62-1 | Saturation, 23°C, by immersion |
粘度 | *** Pa-s | ISO 11443 | Melt Viscosity, 400°C |
螺旋流 | *** mm | - | 415°C nozzle, 220°C tool, 1mm thick |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** Mpa | ISO 527 | 23°C |
拉伸强度 | |||
屈服(yld) | *** Mpa | ISO 527 | 23°C |
拉伸延伸率 | |||
断裂(brk) | *** % | ISO 527 | 23°C |
弯曲模量 | *** Mpa | ISO 178 | 23°C |
弯曲强度 | |||
屈服(yld) | *** Mpa | ISO 178 | 23°C |
3.5%应变 | *** Mpa | ISO 178 | 23°C |
- | *** Mpa | ISO 178 | 125°C |
- | *** Mpa | ISO 178 | 175°C |
- | *** Mpa | ISO 178 | 275°C |
抗压强度 | *** Mpa | ISO 604 | 120°C |
抗压强度 | *** Mpa | ISO 604 | 200°C |
抗压强度 | *** Mpa | ISO 604 | 23°C |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | *** kJ/m² | ISO 180/U | |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
邵氏硬度 D | *** D | ISO 868 | 23°C |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | |
比热容 | *** J/g-°C | DSC | 23°C |
线性膨胀系数(CLTE) | |||
纵向(Flow) | *** E-6/K | ISO 11359 | Along flow above Tg |
纵向(Flow) | *** E-6/K | ISO 11359 | Along flow above Tg |
横向(Across Flow) | *** E-6/K | ISO 11359 | Average above Tg |
横向(Across Flow) | *** E-6/K | ISO 11359 | Average above Tg |
熔融温度(Tm) | *** °C | ISO 11357 | |
玻璃化温度(Tg) | *** °C | ISO 11357-2 | Onset |
玻璃化温度(Tg) | *** °C | ISO 11357 | Midpoint |
导热系数 | *** W/(m K) | ISO 22007-4 | Along flow, 23°C |
导热系数 | *** W/(m K) | ISO 22007-4 | Average, 23°C |
加工温度 | ***~*** °C | - | |
模具温度 | ***~*** °C | - | |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
灼热丝可燃性指数(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | 2mm thickness |
| 电学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
体积电阻率 | *** Ohm-cm | IEC 60093 | 125°C |
体积电阻率 | *** Ohm-cm | IEC 60093 | 23°C |
体积电阻率 | *** Ohm-cm | IEC 60093 | 275°C |
相对漏电起痕指数(CTI ) | |||
- | *** V | IEC 60112 | |
绝缘强度 | *** kV/mm | IEC 60243-1 | 2mm thickness |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。