DOWLEX™ Polyethylene Resin is designed for the production of a wide variety of film applications. Films made from this resin exhibit a combination of good toughness and tear resistance.
Complies with:
U.S. FDA FCN 741
HPFB (Canada), No Objection
EU, No 10/2011
Consult the regulations for complete details.
| Original Document | Technical Datasheet(English) | |||
| Processing | Blown Film | |||
| Compliance | EU 2011/10/ECFDAHPFB (Canada) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Density/Specific Gravity | *** g/cm³ | Internal | Base Density |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Melt Temperature(Tm) | *** °C | Internal | DSC |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | 50.8 µm |
Gloss | *** - | ASTM D 2457 | 45°, 50.8 µm |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | MD, 51 µm |
Yield | *** Mpa | ASTM D 882 | TD, 51 µm |
Break | *** Mpa | ASTM D 882 | MD, 51 µm |
Break | *** Mpa | ASTM D 882 | TD, 51 µm |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD, 51 µm |
Break | *** % | ASTM D 882 | TD, 51 µm |
Puncture resistance | *** J/cm³ | Internal | 51 µm |
Elmondorf Tear | *** g | ASTM D 1922 | MD, 51 µm |
Elmondorf Tear | *** g | ASTM D 1922 | TD, 51 µm |
Secant Modulus | *** Mpa | ASTM D 882 | 2% Secant, MD, 51 µm |
Secant Modulus | *** Mpa | ASTM D 882 | 2% Secant, TD, 51 µm |
Dart Drop Impact | *** g | ASTM D 1709 | 51 µm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.