| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ISO 1183 | |
密度/比重 |
*** g/cm³
| ISO 1183 | Black 2.5 mm thick sheet |
熔体质量流动速率(MFR) | | | |
190℃/2.16 kg |
*** g/10min | ISO 1133 | |
190℃/5 kg |
*** g/10 min | ISO 1133 | |
环境应力开裂(ESCR ) |
*** Hours
| ASTM D 1693 | 20°C, 2.00 mm, 10% Antarox, Compression Molded |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
*** Mpa | ISO 527-2 | Black 2.5 mm thick sheet |
屈服(yld) |
*** Mpa | ISO 527-2/50 | 2.00 mm, Compression Molded |
断裂(brk) |
*** Mpa | ISO 527-2 | Black 2.5 mm thick sheet |
断裂(brk) |
*** Mpa | ISO 527-2/50 | 2.00 mm, Compression Molded |
拉伸延伸率 | | | |
屈服(yld) |
*** % | ISO 527-2 | Black 2.5 mm thick sheet |
屈服(yld) |
*** % | ISO 527-2/50 | 2.00 mm, Compression Molded |
断裂(brk) |
*** % | ISO 527-2 | Black 2.5 mm thick sheet |
断裂(brk) |
*** % | ISO 527-2/50 | 2.00 mm, Compression Molded |
弯曲模量 |
*** Mpa
| ISO 178 | 2% Secant, 2.00 mm, Compression Molded |
撕裂强度 |
*** N
| DIN 53356 | Black 2.5 mm thick sheet |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-40℃ (-40℉) |
*** kJ/m² | ISO 180 | 2.00 mm, Compression Molded |
23℃ (73℉) |
*** kJ/m² | ISO 180 | 2.00 mm, Compression Molded |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
邵氏硬度 D |
*** D
| ISO 868 | 2.00 mm, Compression Molded |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
维卡软化温度(Vicat) |
*** °C
| ISO 306/A120 | |
| 薄膜性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
穿透强度 |
*** N
| DIN 54307 | Black 2.5 mm thick sheet |
| 其他性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
氧化诱导期(OIT) |
*** Min
| EN 728 | 210°C |