DOWLEX™ 2045G Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films . Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery.
Linear Low Density Polyethylene
For heavy duty applications
Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a.
Consult the regulations for complete details.
| 原厂资料 | 物性表(英文) | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D792 | |
密度 | 0.92 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 106 °C | ASTM D1525 | |
熔融温度(Tm) | 119 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 10 % | ASTM D1003 | |
光泽度 | 60 - | ASTM D 2457 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11.3 Mpa | ASTM D 882 | MD |
屈服(yld) | 11.9 Mpa | ASTM D 882 | TD |
断裂(brk) | 47.4 Mpa | ASTM D 882 | MD |
断裂(brk) | 40.6 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 600 % | ASTM D 882 | MD |
断裂(brk) | 740 % | ASTM D 882 | TD |
穿透强度 | 62.3 N | Internal | |
耐穿透性 | 26.1 J/cm³ | Internal | |
耐穿透性 | 5.31 J | Internal | |
抗拉韧性 | 118 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 129 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 370 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 630 g | ASTM D 1922 | TD |
割线模量 | 237 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 275 Mpa | ASTM D 882 | 1% Secant, TD |
割线模量 | 205 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 232 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 220 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。