CONTINUUM DGDA-2488 NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. It is specifically designed for use in all duct and cable in conduit (CIC) applications for both telecommunications and power cables. Typical uses include high performance conduit for fiber optic networks and 5G expansion. The natural resin combined with color concentrate can be readily processed by any current duct or conduit extrusion method in all sizes at commercial rates.
Industrial Standards Compliance:
ASTM D 3350: cell classification PE435440A
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 加工助剂 | |||
| 成型方式 | 管材挤出 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.954 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.28 g/10min | ASTM D1238 | |
190℃/21.6 kg | 27 g/10 min | ASTM D 1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | 50°C, 100% Igepal, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22.8 Mpa | ASTM D638 | |
断裂(brk) | 31.7 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 3.7 % | ASTM D638 | |
断裂(brk) | 750 % | ASTM D638 | |
弯曲模量 | 1000 Mpa | ASTM D790 | 2% Secant |
管材缺口拉伸实验 | 10 hr | ASTM F1473 | PENT, 80°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -60 °C | ASTM D 746 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 132 °C | Internal | DSC |
结晶温度 | 118 °C | Internal | DSC |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。