For packaging and food packaging applications
Offers high pinhole resistance, excellent flexibility and abuse resistance
Excellent sealing characteristics
Offers toughness, seal properties, optical properties and processability
Complies with:
U.S. FDA FCN 424
U.S. FDA-DMF
U.S. USP
EU, No 10/2011
CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS)
Japan Hygienic Olefin and Styrene Plastics Association
Consult the regulations for complete details.
| 原厂资料 | 物性表-ASTM(英文) | |||
| 法规认证 | DMF(药品主控文件)EU 2011/10/EC (欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局)JHOSPA(日本卫生级烯烃与苯乙烯塑料协会) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ASTM D792 | |
密度 | 0.905 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.8 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 83.9 °C | ASTM D1525 | |
熔融温度(Tm) | 123 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 14 % | ASTM D1003 | |
光泽度 | 39 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6.21 Mpa | ASTM D 882 | MD |
屈服(yld) | 5.86 Mpa | ASTM D 882 | TD |
断裂(brk) | 32.4 Mpa | ASTM D 882 | MD |
断裂(brk) | 30 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 340 % | ASTM D 882 | MD |
断裂(brk) | 570 % | ASTM D 882 | TD |
穿透强度 | 48.9 N | Internal | 25 µm |
耐穿透性 | 24.8 J/cm³ | Internal | 25 µm |
耐穿透性 | 4.52 J | Internal | 25 µm |
抗拉韧性 | 45.5 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 64.5 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 370 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 520 g | ASTM D 1922 | TD |
割线模量 | 98.6 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 113 Mpa | ASTM D 882 | 1% Secant, TD |
割线模量 | 89.6 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 93.8 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 1100 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。