Queo 0201 is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst.
CAS-No. 26221-73-8
Applications
Queo 0201 Demonstrated applications include: Seal layers in lamination and flexible barrier films High strength flexible films Heat shrinkable display film Specialty stretch film applications PP film toughness modification Roof coverings Tunnel linings Flexible low voltage insulation Halogen free flame retardant compounds Blow moulding Soft foams, e.g. artificial wine corks
Additives
Queo 0201 contains processing stabilizers
Special Features
Queo 0201 is optimised to deliver: Excellent environmental stress cracking resistance (ESCR) High clarity Flexibility Versatile blending with other polyolefins in film, extrusion and moulding applications. Unrivalled sealing and hot tack properties at low temperature Low amount of extractables Outstanding toughness Outstanding puncture resistance Low temperature impact strength
| 原厂资料 | 物性表-ISO(英文) Queo™各牌号物性概要(英文) | |||
| 产品特性 | 耐低温冲击良好柔韧性阻燃无卤ESCR | |||
| 添加助剂 | 加工助剂 | |||
| 成型方式 | 注塑挤出薄膜挤出吹塑共混改性 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.902 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.1 g/10min | ISO 1133 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 36 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 715 % | ISO 527-2 | |
弯曲模量 | 72 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | NB kJ/m² | ISO 180/1A | |
脆化温度 | -90 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 43 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 82 °C | ISO 306 | 10 N |
熔融温度(Tm) | 97 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 2 % | ASTM D1003 | |
光泽度 | 84 - | ASTM D 2457 | 45 °C |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸模量 | 65 Mpa | ASTM D 882 | |
穿透强度 | 2800 J/m | Internal | |
落锤冲击 | 48 g/µm | ASTM D 1709 | |
低密封初始温度(SIT) | 78 ℃ | ASTM F88 |