Borstar FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness.
Borstar FB1350 is well suited for mono- and coextrusion of films produced with high neck or low neck extrusion.
Applications
Borstar FB1350 has been developed especially for applications like: Heavy-duty sack General packaging Pouches Refuse sacks and liners Geomembranes Blending
Additives
Borstar FB1350 contains antioxidant.
| 原厂资料 | 物性表-ISO(英文) | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 挤出薄膜挤出共挤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.935 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.6 g/10 min | ISO 1133 | |
190℃/21.6 kg | 15 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.4 - | ISO 8295 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 127 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 80 % | ASTM D1003 | |
光泽度 | 5 - | ASTM D 2457 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 57 Mpa | ISO 527-3 | MD |
- | 48 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 400 % | ISO 527-3 | MD |
断裂(brk) | 650 % | ISO 527-3 | TD |
拉伸模量 | 500 Mpa | ISO 527-3 | MD |
拉伸模量 | 650 Mpa | ISO 527-3 | TD |
埃尔曼多夫撕裂 | 12 N | ISO 6383-2 | MD |
埃尔曼多夫撕裂 | 290 N | ISO 6383-2 | TD |
落锤冲击 | 150 g | ISO 7765-1 | |
落锤冲击 | 15 J/mm | ISO 7765-2 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。