BorShape FX1002 is a blown film grade.
It is a high alpha olefin terpolymer polyethylene film grade combining excellent extrusion behaviour and superior mechanical properties which are kept in cold conditions.
BorShape™ FX1002 has been specially developed to deliver high throughput while achieving high toughness and high stiffness levels.
Applications
BorShape FX1002 is designed for: Flexible packaging Frozen food packaging Lamination films Heavy-duty bags Medium duty bags Agricultural films Refuse bags Liquid packaging Collation shrink
Additives
BorShape FX1002 contains antioxidant
| 原厂资料 | 物性表-ISO(英文) | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.937 g/cm³ | ISO 1183 | Base Resin |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 2 g/10 min | ISO 1133 | |
190℃/21 kg | 42 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.4 - | ISO 8295 | Dynamic |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 113 °C | ISO 306 | |
熔融温度(Tm) | 128 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 60 % | ASTM D1003 | |
光泽度 | 10 - | ASTM D 2457 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 55 Mpa | ISO 527-3 | MD |
- | 40 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 550 % | ISO 527-3 | MD |
断裂(brk) | 750 % | ISO 527-3 | TD |
拉伸模量 | 450 Mpa | ISO 527-3 | MD |
拉伸模量 | 550 Mpa | ISO 527-3 | TD |
埃尔曼多夫撕裂 | 35 N | ISO 6383-2 | MD |
埃尔曼多夫撕裂 | 200 N | ISO 6383-2 | TD |
落锤冲击 | 250 g | ISO 7765-1 | |
落锤冲击 | 18 J/mm | ISO 7765-2 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。