BorShape FX1001 is a blown film grade.
It is a high alpha olefin terpolymer polyethylene film grade combining very good extrusion behaviour and superior mechanical properties, which are kept in cold conditions
BorShape FX1001 has been developed especially for applications requiring high toughness at high stiffness levels.
Applications
BorShape FX1001 is designed for: Flexible packaging Frozen food packaging Lamination films Heavy-duty bags Medium duty bags Agricultural films Refuse bags Liquid packaging Collation shrink
Additives
BorShape FX1001 contains antioxidant
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 抗氧化 | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.931 g/cm³ | ISO 1183 | Base Resin |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.9 g/10 min | ISO 1133 | |
190℃/21 kg | 20 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.4 - | ISO 8295 | Dynamic |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 127 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 80 % | ASTM D1003 | |
光泽度 | 7 - | ASTM D 2457 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 50 Mpa | ISO 527-3 | MD |
- | 40 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 450 % | ISO 527-3 | MD |
断裂(brk) | 700 % | ISO 527-3 | TD |
拉伸模量 | 350 Mpa | ISO 527-3 | MD |
拉伸模量 | 450 Mpa | ISO 527-3 | TD |
埃尔曼多夫撕裂 | 60 N | ISO 6383-2 | MD |
埃尔曼多夫撕裂 | 250 N | ISO 6383-2 | TD |
落锤冲击 | 480 g | ISO 7765-1 | |
落锤冲击 | 28 J/mm | ISO 7765-2 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。