Bormed RF830MO is a polypropylene random copolymer intended for evaluation for use in Healthcare applications.
This transparent grade is modified with a nucleating agent and is suitable for articles, which need post sterilisation with radiation. Bormed RF830MO is characterised by easy processability, high transparency, high gloss and a good stiffness-impact balance. Products moulded from this grade and radiated with the dose of 25 kGy have a shelf-life of 5 years, if properly stored. Material can also be sterilised with ethylene oxide and steam.
CAS-No. 9010-79-1
Applications
Bormed RF830MO has been evaluated according to different regulations and norms. Typical applications are mentioned below for Medical and Diagnostic devices or Pharmaceutical packaging. However, Borealis should be consulted for final approval to evaluate the use of Bormed RF830MO .
Disposable non pre-filled syringes Needle hubs Catheter connections Laboratory disposable Diagnostic products Blood collection tubes
The customer should be aware that Bormed products may only be used in applications which are pre-approved for evaluation by Borealis received in the form of a risk assessment form (RAF) review response. Without such preapproval, no use of the grade shall be made. In case of doubt, the customer should seek pre-approval for evaluation from Borealis to proceed through their Sales or technical contact. Borealis makes no warranties beyond what is contained in this product datasheet and the customer is responsible for reading and accepting the disclaimer as contained in this product datasheet.
Special Features
Radiation resistance High transparency Easy processing
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good StiffnessGood Impact ResistanceLight TransmissionHigh GlossEasy processingMedical Application/Health CareGamma ResistanceEtO sterilizableSteam Resistant | |||
| Additive | Nucleating Agent | |||
| Appearance | Clear/Transparent | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.