PS65T20 is a 20% mineral filled polypropylene compound intended for injection and back injection moulding. This material has excellent balanced mechanical properties and high melt flow rate.
Applications
PS65T20 has been developed especially for the car industry to be used in automotive interior parts. Trunk claddings Automotive interior applications
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高流动填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 矿物 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 23 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 32 Mpa | ISO 527-2 | 50 mm/min |
弯曲模量 | 2700 Mpa | ISO 178 | 2 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 2 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 3 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 110 °C | ISO 75-2 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
凝雾实验 | |||
- | 2 mg | DIN 75201 | 100 °C,16 h |
VOC挥发 | 50 µgC/g | VDA 277 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。