Fibremod GB215HP-9502 is a 20 % long glass fibre reinforced polypropylene grade intended for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing outstanding mechanical properties such as high strength, high stiffness and excellent impact behaviour.
Due to its excellent combination of properties this material can substitute in many applications other engineering plastics or metal alloys. A significant value of this material is the fact that it does not change its mechanical properties at humid conditions or water contact.
The product is available in standard black 9502.
| Original Document | Technical Datasheet-ISO(English) Summary Data Sheets-Automotive(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat StabilizedFoamableFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Black | |||
| Processing | InjectionExtrusion | |||
| Reinforced | 20% Long Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Molding Shrinkage | |||
Flow | *** % | Internal | 150x80x2 mm |
Across Flow | *** % | Internal | 150x80x2 mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Fogging | |||
- | *** mg | DIN 75201 | 100 °C,16 h |
Volatile Organic Compounds | *** µgC/g | VDA 277 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.