35% glass fiber reinforced, heat stabilized Polyamide 66
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | PA66-GF35 | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfrica | |||
| Features | High StrengthHeat StabilizedGood Heat AgingOil ResistantMedium viscosityFilled & Reinforced | |||
| Appearance | Colors Available | |||
| Processing | Injection | |||
| Automotive Specs | FORD WSK-M4D673-AGM(General Motors) GMW3038P-PA66-GF35J Color: NaturalGM(General Motors) QK 003014 H Color: 96.8001 Black | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateStress-strainSecant modulus-strainTensile modulus-temperature | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
Viscosity | *** cm³/g | ISO 307 | Viscosity Number |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | Conditioned |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A/5 | |
Break | *** Mpa | ISO 527-2/1A/5 | Conditioned |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A/5 | |
Break | *** % | ISO 527-2/1A/5 | Conditioned |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Conditioned |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Conditioned |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746 | |
1.5/1.6 mm | *** °C | UL 746 | |
3.0/3.2 mm | *** °C | UL 746 | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746 | |
1.5/1.6 mm | *** °C | UL 746 | |
3.0/3.2 mm | *** °C | UL 746 | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746 | |
1.5/1.6 mm | *** °C | UL 746 | |
3.0/3.2 mm | *** °C | UL 746 | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
Glow Wire Flammability Index(GWFI) | |||
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
FMVSS | *** mm/min | FMVSS 302 | |
Burning Rate | *** mm/min | ISO 3795 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | Conditioned |
Surface Resistivity | *** Ohm | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | Conditioned |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.