30% glass fibre reinforced flame-retardant Polyamide 6 grade; halogen free
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Flame RetardantHalogen FreeFilled & Reinforced | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Viscosity | *** cm³/g | ISO 307 | Viscosity Number |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | Conditioned |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A/5 | |
Break | *** Mpa | ISO 527-2/1A/5 | Conditioned |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A/5 | |
Break | *** % | ISO 527-2/1A/5 | Conditioned |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Conditioned |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Conditioned |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | Pass |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | IEC 60695-11-10 | |
V-0 | *** mm | IEC 60695-11-10 | |
V-0 | *** mm | IEC 60695-11-10 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
Burning Rate | mm/min | ISO 3795 | 0.750 mm, Self-Extinguishing |
Burning Rate | mm/min | ISO 3795 | 1.50 mm, Self-Extinguishing |
Burning Rate | mm/min | ISO 3795 | 3.00 mm, Self-Extinguishing |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.