30% glass fibre reinforced PBT/PET compound based on post consumer PET
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | (PBT+PET)-GF30 | |||
| Availability | AsiaEuropeMiddle EastAfrica | |||
| Features | Filled & ReinforcedRecycled Contained | |||
| Processing | Injection | |||
| Automotive Specs | FORD WSB-M4D921-A Color: BlackGM(General Motors) GMW15702-019101 PBT+PET-GF30 Color: 96.8001 BlackGM(General Motors) GMW15702-019102 PBT+PET-GF30 Color: 96.8001 LS BlackGM(General Motors) GMW15702-019103 PBT+PET-GF30 Color: 96.8082 LM BlackGM(General Motors) GMW15702-019104 PBT+PET-GF30 Color: 96.8069 LW Black | |||
| Diagrams | Viscosity-shear rateShearstress-shear rate | |||
| Recycled Content | Post Consumer Recycled | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
260°C/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A/5 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A/5 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | H 961/30 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | PASS |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** mm/min | FMVSS 302 | 2.00 mm |
Burning Rate | *** mm/min | ISO 3795 | 2.00 mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.