Schulablend M/MA 5310U is an UV stabilized PC/ASA alloy. Injection molding grade
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Good Impact ResistanceHeat ResistanceUV StabiltiyWeather Resistance | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
265°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 1.0 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 50 mm/min |
Break | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Loading 1 (10 N) |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Loading 2 (50 N) |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
FMVSS | *** mm/min | FMVSS 302 | |
Burning Rate | *** mm/min | ISO 3795 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.