10% mineral filled PA-PP-Blend with high chemical resistance and reduced moisture absorption. (Former name: SCHULABLEND® MK10)
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Chemical ResistanceLow Moisture AbsorptionFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 10% Mineral | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
250℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A/50 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/1A/50 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ASTM D256 | Area |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
Glow Wire Flammability Index(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | |
FMVSS | *** mm/min | FMVSS 302 | 2.00 mm |
Burning Rate | *** mm/min | ISO 3795 | 2.00 mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | *** Ohm | IEC 60093 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.