Purell PE 1840H is a low density polyethylene with good flexibility and delivered in pellet form. It is used by our customers mainly for small blow moulding of heathcare applications such as ampoules but can also be used in film applications and injection moulding.
| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) | |||
| 产品特性 | 良好柔韧性医疗级环氧乙烷灭菌(EtO) | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 注塑吹塑挤出吹塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.919 g/cm³ | ISO 1183 | |
密度 | 0.919 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.5 g/10min | ISO 1133 | |
190℃/2.16 kg | 1.5 g/10min | ASTM D1238 | |
堆积(视)密度 | 0.5 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 1560 psi | ASTM D638 | |
屈服(yld) | 9 Mpa | ISO 527-1/-2 | 23 °C |
断裂(brk) | 1770 psi | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 15 % | ISO 527-1/-2 | |
断裂(brk) | 670 % | ASTM D638 | |
弯曲模量 | 35000 psi | ASTM D790 | 1% Secant |
拉伸模量 | 36900 psi | ASTM D638 | 1% Secant |
拉伸模量 | 200 Mpa | ISO 527-1/-2 | 23 °C |
摩擦系数 | 75 - | ISO 8295 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 45 D | ISO 868 | |
邵氏硬度 D | 47 D | ISO 868 | |
邵氏硬度 D | 47 D | ASTM D 2240 | |
球压硬度 | 15 Mpa | ISO 2039-1 | H 49/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 87 °C | ASTM D1525 | |
维卡软化温度(Vicat) | 88 °C | ISO 306/A50 | |
熔融温度(Tm) | 108 °C | ISO 3146 | |
加工温度 | 170~220 °C | - | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11 % | ASTM D1003 | 50 µm |
光泽度 | 75 - | ASTM D 523 | Gardner Gloss (60°) |
光泽度 | 20 - | ASTM D 2457 | Gloss (20°, 50 µm) |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 17 Mpa | ISO 527-1/-3 | |
- | 27 Mpa | ISO 527-1/-3 | |
拉伸延伸率 | |||
断裂(brk) | 200 % | ISO 527-1/-3 | |
断裂(brk) | 600 % | ISO 527-1/-3 | |
落锤冲击 | 120 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。