Pro-fax 8523 very high impact polypropylene copolymer is available in pellet form. This resin is typically used in extrusion or injection molding applications and offers excellent low temperature impact resistance.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax 8523.
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Features | High ImpactHigh Impact at Low TemperaturCopolymer | |||
| Appearance | Pellets/Granules | |||
| Processing | InjectionExtrusionSheet ExtrusionProfile Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23 °C, Method A |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23 °C |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 50 mm/min |
Yield | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Yield | *** % | ISO 527-1/-2 | 23 °C |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 1% Secant, Procedure A |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | when Complete Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | when Partial/Hinge Breaks |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | Method A |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.