NORYL EM7304F resin is a 15% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade has enhanced polyurethane foam adhesion and high flow along with creep resistance, dimensional stability, and hydrolytic stability. NORYL EM7304F resin is an excellent candidate for automotive interior applications such as instrument panel retainers.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 尺寸稳定抗蠕变良好粘合性耐水解高流动填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 15% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.15 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.2~0.3 % | Internal | 3.2 mm |
横向(Across Flow) | 0.25~0.45 % | Internal | 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 77 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ASTM D638 | Type I, 5 mm/min |
弯曲应变 | |||
屈服(yld) | 108 % | ASTM D 790 | 2.6 mm/min, 100 mm span |
弯曲模量 | 4550 Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 64 J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 6.4 mm, unannealed |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。