Petrothene GA808091 is a broad molecular weight, linear low density polyethylene resin selected by customers for use as a base resin in wire and cable jacketing. An antioxidant package is added to ensure thermal stability during processing.
Petrothene GA808091 meets the requirements of the following: ASTM D 1248, Type I, Class A, Category 4, Grade E5; Federal LP390C, Type II, Class L, Category 4, Grade 4.
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Heat StabilizedOxidation stability | |||
| Additive | Antioxidant | |||
| Processing | Wire & Cable Extrusion | |||
| Compliance | ASTM D1248FED L-P-390C | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | 23 °C |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
Environmental Stress Cracking Resistance | *** Hours | ASTM D 1693 | F50 (10% Igepal®, Cond A) |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Brittleness Temperature | *** °C | ASTM D 746 | F50 |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ASTM D 2240 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
1MHz | *** E-4 | ASTM D150 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.