Hostalen GM 5010 T3 black is a high density polyethylene (HDPE), black colored similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 80 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
This grade is not intended for medical and pharmaceutical applications.
This grade is supported for use in drinking water applications.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good Heat AgingWear/Abrasion ResistanceCreep ResistantGood WeldDrinking Water ContactUV StabiltiyWeather ResistanceESCRChemical ResistanceHigh Viscosity | |||
| Appearance | Black | |||
| Processing | InjectionExtrusionCompression Moulding | |||
| Reinforced | 2.25% Carbon black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/5 kg | *** g/10 min | ISO 1133 | |
190℃/21.6 kg | *** g/10 min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 23 °C, 50 mm/min |
Break | *** % | ISO 527-1/-2 | 23 °C |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | 2 MPa |
1000h | *** Mpa | ISO 899-1 | 2 MPa |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 1 min |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 2000 hr |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 24 hr |
FNCT | *** hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | 3 sec |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Melt Temperature(Tm) | *** °C | DSC | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxidative Induction Time | *** Min | ISO 11357 | 210 °C |
Minimum Required Strength(MRS) | *** Mpa | ISO 9080 | |
Odor Threshold | *** - | EN 1622/EN 1420 | measured on pellets / 30°C / 4 h extraction time |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.