Hostalen CRP 100 RCD black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100. This new generation of HDPE material has been designed to meet new technical requirements for drinking water piping systems. The material exibits an improved resistance against water disinfectants.
The product provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength, making it the ideal choice for trenchless installation techniques (PE100 RC).
Hostalen CRP 100 RCD black is compliant to existing standards for drinking water piping systems, such as ISO 4427 and EN 12201.
This grade is not intended for medical and pharmaceutical applications.
This grade is supported for use in drinking water applications.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good Heat AgingWear/Abrasion ResistanceCreep ResistantGood WeldDrinking Water ContactUV StabiltiyWeather ResistanceESCRChemical ResistanceDisinfectants ResistantHigh Viscosity | |||
| Appearance | Black | |||
| Processing | InjectionExtrusionCompression Moulding | |||
| Compliance | EN 12201ISO 4427 | |||
| Reinforced | 2.25% Carbon black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/5 kg | *** g/10 min | ISO 1133 | |
190℃/21.6 kg | *** g/10 min | ISO 1133 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 23 °C, 50 mm/min |
Break | *** % | ISO 527-1/-2 | 23 °C |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | 2 MPa |
1000h | *** Mpa | ISO 899-1 | 2 MPa |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 1 min |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 2000 hr |
Flexural Creep Modulus | *** Mpa | DIN 16841 | 4-point loading / 24 hr |
FNCT | *** hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | 3 sec |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Melt Temperature(Tm) | *** °C | DSC | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxidative Induction Time | *** Min | ISO 11357 | 210 °C |
Odor Threshold | *** - | EN 1622/EN 1420 | measured on pellets / 30°C / 4 h extraction time |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.