Hostacom X M2 R13 351236 is a 20% mineral filled elastomer modified polypropylene copolymer. Used for automotive interior trim parts, in particular for instrument panels.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Toughened/Impact ModifiedCopolymerFilled & Reinforced | |||
| Additive | Impact Modifier | |||
| Reinforced | 20% MineralElastomer | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Secant |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
0℃ (32℉) | *** kJ/m² | ISO 179 | Type 1, Edgewise, Notch A, Hinged Break |
23℃ (73℉) | *** kJ/m² | ISO 179 | Type 1, Edgewise, Notch A, Hinged Break |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | Type 1, Edgewise |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | H 358/30 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | A50 (50°C/h 10N) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.