Hostacom TRC 104N D63104 Is a mineral filled high impact, high stiffness polypropylene copolymer. The grade has been specially developed for large complex parts that require good impact as well as good
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | High Stiffness/RigidityHigh ImpactEasy processingGood PaintablilityHigh FlowCopolymerFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | Mineral | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Method A |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | 23 °C, v = 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Type 1, Notch A |
23℃ (73℉) | *** kJ/m² | ISO 180 | Type 1, Notch A |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.