Hostacom G3 U01 102297 is a 30% glass fiber reinforced PP homopolymer, with high melt flow rate, high stiffness and low creep under load at elevated temperatures. This grade is delivered in 102297 color version.
This grade is not intended for medical, pharmaceutical, food and drinking water applications.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | High Stiffness/RigidityCreep ResistantHigh FlowHomopolymerFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23 °C |
Melt Volume Flow Rate(MVR) | |||
230℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 23 °C |
Break | *** % | ISO 527-1/-2 | 23 °C, 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.