Hifax DX277 medium high melt flow, 1,000 MPa flexural modulus, thermoplastic elastomeric olefin (TEO) nanocomposite has an excellent balance of properties and processability. It is characterized by an exceptional impact/stiffness balance, which is attainable at very low density. As a result, parts molded from DX277 are light in weight and exhibit good toughness characteristics.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good StiffnessGood Impact ResistanceDimensional StabilityGood PaintablilityHigh FlowLow Density | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180 | |
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-1/-2 | -30°C to 100°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.