Hifax CA 7271 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology.
It is designed for injection molding controlled shrinkage applications (e.g. bumpers). Hifax CA 7271 A exhibits high melt flow rate with good impact/stiffness balance and reduced shrinkage.
The grade is available in natural pellet form.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | High Stiffness/RigidityHigh ImpactLow GlossDimensional StabilityEasy processingGood PaintablilityGood Adhesion | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | InjectionCompounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23 °C, Method A |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | |
Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179 | |
-20℃ (-4℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Melt Temperature(Tm) | *** °C | DSC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.