Hifax CA 10 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell proprietary Catalloy process technology. It is suitable for industrial applications where a combination of good processability and excellent softness is required. It is widely used as building block resin for flexible water-proofing membranes.
Hifax CA 10 A exhibits low stiffness, low hardness and good impact resistance. The grade is available in natural pellet form.
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 良好冲击性耐热易成型ESCR软质 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 压延挤出线缆挤出吹塑热成型共混改性 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.88 g/cm³ | ISO 1183 | 23 °C, Method A |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.6 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 11 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 500 % | ISO 527-1/-2 | |
弯曲模量 | 90 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 5 kJ/m² | ISO 179 | Complete Break |
-20℃ (-4℉) | 110 kJ/m² | ISO 179 | Partial Break |
23℃ (73℉) | NB kJ/m² | ISO 179 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 30 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 40 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 60 °C | ISO 306/A50 | |
熔融温度(Tm) | 142 °C | ISO 11357-3 | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
光泽度 | 85 - | ASTM D 2457 | 60°, 45 mil |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。