| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
220℃/10 kg |
*** g/10 min | ASTM D 1238 | |
230°C/3.8 kg |
*** g/10 min | ASTM D 1238 | |
收缩率 | | | |
纵向(Flow) |
*** % | ASTM D955 | 48 hr |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
*** Mpa | ASTM D638 | 23°C, 3.18 mm, Injection Molded, 50 mm/min |
断裂(brk) |
*** Mpa | ASTM D638 | 23°C, 3.18 mm, Injection Molded, 50 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
*** % | ASTM D638 | 23°C, Injection Molded, 50 mm/min |
弯曲模量 |
*** Mpa
| ASTM D790 | 23°C, 3.18 mm, Injection Molded, 1.3 mm/min |
弯曲强度 | | | |
- |
*** Mpa | ASTM D790 | 23°C, 3.18 mm, Injection Molded, 1.3 mm/min |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-20℃ (-4℉) |
*** J/m | ASTM D256 | 3.18 mm |
0℃ (32℉) |
*** J/m | ASTM D256 | 3.18 mm |
23℃ (73℉) |
*** J/m | ASTM D256 | 3.18 mm, Injection Molded |
仪器化落镖冲击能量 | | | |
- |
*** J | ASTM D3763 | 0°C, 2.04 m/sec |
- |
*** J | ASTM D3763 | 23°C, 2.04 m/sec |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | Unannealed |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate A (50°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) |
*** °C
| ASTM D1525 | Rate B (120°C/h), Loading 2 (50 N) |
| 光学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
光泽度 |
*** -
| ASTM D 523 | 60° |