| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.17 g/cm³
| ISO 2781 | |
比重 | 1.17 g/cm³
| ASTM D471 | |
收缩率 | | | |
纵向(Flow) |
3 % | ASTM D 955 | 1.59 mm |
纵向(Flow) |
2 % | ASTM D 955 | 3.18 mm |
横向(Across Flow) |
0.5 % | ASTM D 955 | 1.59 mm |
横向(Across Flow) |
1.5 % | ASTM D 955 | 3.18 mm |
粘度 | 700 Pa-s
| ASTM D 3835 | Melt Viscosity (190°C, 300 sec^-1) |
磨耗 | 3 mg/1000cy
| ASTM D 1044 | 1000 g, CS-17 Wheel |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
12.1 Mpa | ASTM D 412 | 1.90 mm, Compression Molded |
屈服(yld) |
11 Mpa | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
屈服(yld) |
11 Mpa | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
屈服(yld) |
12.1 Mpa | ISO 37 | 1.90 mm, Compression Molded |
100%延伸率时 |
6.2 Mpa | ASTM D 412 | 1.90 mm, Compression Molded |
100%延伸率时 |
6.2 Mpa | ISO 37 | 1.90 mm, Compression Molded |
100%延伸率时 |
5.2 Mpa | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
100%延伸率时 |
5.2 Mpa | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
拉伸延伸率 | | | |
断裂(brk) |
320 % | ASTM D 412 | 1.90 mm, Compression Molded |
断裂(brk) |
320 % | ISO 37 | 1.90 mm, Compression Molded |
断裂(brk) |
240 % | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
断裂(brk) |
240 % | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
撕裂强度 | 35 kN/m
| ASTM D 624 | Die C, 1.90 mm, Compression Molded |
压缩永久形变 | 62 %
| ASTM D 395 | 100°C, 22 hr |
压缩永久形变 | 14 %
| ASTM D 395 | 24°C, 22 hr |
压缩永久形变 | 62 %
| ISO 815 | 100°C, 22 hr |
压缩永久形变 | 14 %
| ISO 815 | 24°C, 22 hr |
拉伸形变 | 10 %
| ASTM D 412 | 1.90 mm, Compression Molded |
扭转模量 | 27.5 Mpa
| ASTM D1043 | -20°C, 1.90 mm, Compression Molded |
扭转模量 | 3.2 Mpa
| ASTM D1043 | 24°C, 1.90 mm, Compression Molded |
Clash-Berg模量 | 68.9 Mpa
| ASTM D1043 | -17°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -86 °C
| ASTM D 746 | |
脆化温度 | -86 °C
| ISO 812 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 78 A
| ASTM D 2240 | 1.90 mm, Compression Molded |
邵氏硬度 A | 78 A
| ISO 868 | 1.90 mm, Compression Molded |
| 老化性能 | 值/单位 | 测试标准 | 测试条件 |
硬度 (热老化) | -2 -
| ISO 188 | Change in Air (Shore A, 125°C, 168 hr) |
硬度 (热老化) | -2 -
| ASTM D573 | Change in Air (Shore A, 125°C, 168 hr) |
体积变化 | -8 %
| ISO 1817 | 100°C, 168 hr, in ASTM #1 Oil |
体积变化 | 31 %
| ISO 1817 | 100°C, 168 hr, in IRM 903 Oil |
体积变化 | 5 %
| ISO 1817 | 100°C, 168 hr, in Water |
体积变化 | 32 %
| ISO 1817 | 27°C, 168 hr, in Reference Fuel B |
体积变化 | -8 %
| ASTM D471 | 100°C, 168 hr, in ASTM #1 Oil |
体积变化 | 31 %
| ASTM D471 | 100°C, 168 hr, in IRM 903 Oil |
体积变化 | 5 %
| ASTM D471 | 100°C, 168 hr, in Water |
体积变化 | 32 %
| ASTM D471 | 27°C, 168 hr, in Reference Fuel B |