| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 2781 | |
Density/Specific Gravity |
*** g/cm³
| ASTM D471 | |
Viscosity |
*** Pa-s
| ASTM D 3835 | Melt Viscosity (190°C, 300 sec^-1) |
Abrasion resistance |
*** mg/1000cy
| ASTM D 1044 | 1000 g, CS-17 Wheel |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | | | |
Yield |
*** Mpa | ASTM D 412 | 1.90 mm, Compression Molded |
Yield |
*** Mpa | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
Yield |
*** Mpa | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
Yield |
*** Mpa | ISO 37 | 1.90 mm, Compression Molded |
at 100% strain |
*** Mpa | ASTM D 412 | 1.90 mm, Compression Molded |
at 100% strain |
*** Mpa | ISO 37 | 1.90 mm, Compression Molded |
at 100% strain |
*** Mpa | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
at 100% strain |
*** Mpa | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
Tensile Elongation | | | |
Break |
*** % | ASTM D 412 | 1.90 mm, Compression Molded |
Break |
*** % | ISO 37 | 1.90 mm, Compression Molded |
Break |
*** % | ASTM D573 | 125°C, 1.90 mm,7 days, Compression Molded |
Break |
*** % | ISO 188 | 125°C, 1.90 mm,7 days, Compression Molded |
Tear Strength |
*** kN/m
| ASTM D 624 | Die C, 1.90 mm, Compression Molded |
Compression Set |
*** %
| ASTM D 395 | 100°C, 22 hr |
Compression Set |
*** %
| ASTM D 395 | 24°C, 22 hr |
Compression Set |
*** %
| ISO 815 | 100°C, 22 hr |
Compression Set |
*** %
| ISO 815 | 24°C, 22 hr |
Tensile Set |
*** %
| ASTM D 412 | 1.90 mm, Compression Molded |
Torsional Modulus |
*** MPa
| ASTM D1043 | -20°C, 1.90 mm, Compression Molded |
Torsional Modulus |
*** MPa
| ASTM D1043 | 24°C, 1.90 mm, Compression Molded |
Clash-Berg Modulus |
*** MPa
| ASTM D1043 | -40°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Brittleness Temperature |
*** °C
| ASTM D 746 | |
Brittleness Temperature |
*** °C
| ISO 812 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness |
*** A
| ASTM D 2240 | 1.90 mm, Compression Molded |
Shore A hardness |
*** A
| ISO 868 | 1.90 mm, Compression Molded |
| Aging | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Hardness(Heat Aging) |
*** -
| ISO 188 | Change in Air (Shore A, 125°C, 168 hr) |
Hardness(Heat Aging) |
*** -
| ASTM D573 | Change in Air (Shore A, 125°C, 168 hr) |
Change in Volume |
*** %
| ISO 1817 | 100°C, 168 hr, in ASTM #1 Oil |
Change in Volume |
*** %
| ISO 1817 | 100°C, 168 hr, in IRM 903 Oil |
Change in Volume |
*** %
| ISO 1817 | 100°C, 168 hr, in Water |
Change in Volume |
*** %
| ISO 1817 | 27°C, 168 hr, in Reference Fuel B |
Change in Volume |
*** %
| ASTM D471 | 100°C, 168 hr, in ASTM #1 Oil |
Change in Volume |
*** %
| ASTM D471 | 100°C, 168 hr, in IRM 903 Oil |
Change in Volume |
*** %
| ASTM D471 | 100°C, 168 hr, in Water |
Change in Volume |
*** %
| ASTM D471 | 27°C, 168 hr, in Reference Fuel B |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.