| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | 23℃ |
Density/Specific Gravity |
*** g/cm³
| ASTM D792 | 23℃ |
Melt Volume Flow Rate(MVR) | | | |
300°C/1.2 kg |
*** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | | | |
300℃/1.2 kg |
*** g/10min | ASTM D1238 | |
Molding Shrinkage | | | |
- |
***~*** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | | | |
Yield |
*** kg/cm² | ASTM D638 | 6 mm/min |
Yield |
*** Mpa | ISO 527 | 50 mm/min |
Break |
*** Mpa | ISO 527 | 50 mm/min |
Tensile Elongation | | | |
- |
*** % | ISO 527 | 50 mm/min |
- |
*** % | ASTM D 638 | 6 mm/min |
Flexural Modulus |
*** kg/cm²
| ASTM D790 | 1.3 mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 2 mm/min |
Flexural Strength | | | |
- |
*** kg/cm² | ASTM D790 | 1.3 mm/min |
- |
*** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 179 | |
Izod Notched Impact Strengh | | | |
23℃ (73℉) |
*** kg·cm/cm | ASTM D256 | 3.2 mm |
23℃ (73℉) |
*** kJ/m² | ISO 180/4A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M |
*** M
| ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75/A | Unannealed |
Vicat Softening Temperature(VST) |
*** °C
| ASTM D1525 | 1KG,50℃/hr |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | 1KG,50℃/hr |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | 5KG,50℃/hr |
Coefficient of Linear Thermal Expansion | | | |
- |
***~*** E-6/°C | ISO 11359 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
V-2 |
*** mm | UL94 | |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.