Adsyl 5 C 37 F is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications.
This grade features a very low seal initiation temperature.
It contains slip and anti-block additives.
For regulatory information please refer to Adsyl 5 C 37 F Product Stewardship Bulletin (PSB).
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Processing | Cast FilmBOPP | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1 mm/min, 1% Secant, Procedure A |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | Method A |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | 50 µm |
Gloss | *** % | ASTM D 2457 | 45°, 50 µm |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Seal Initiation Temperature | *** °C | Internal |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.