Technical Datasheet(English) 

PA6T/6-GF25 FR(52)

Asia

Europe

North America

Middle East

Africa

South & Central America

Flame Retardant

Filled & Reinforced

Dynamic Shear modulus (G storage)-temperature G'|°C|MPa|Temperature in °C|G' in MPa|-20:1726.1@-10:1705.8@0:1695.6@10:1674.2@20:1654@30:1634@40:1609@50:1579.4@60:1518.4@70:1412.2@80:1232@90:817.5@100:495@110:389.3@120:390.1@130:377.5@140:360.7@150:346.3@160:331.4@170:317.6@180:302.6@190:287.1@200:269.2@210:250.6@220:231.1@230:208.5@240:183.9@250:156.3@260:123.3@270:73.59999999999999@280:33.8@290:14.5

Stress-strain -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.29:24.85@0.58:49.46@0.87:73.2@1.16:95.61@1.45:116.34@1.74:135.19@2.03:152.07@2.32:167.02@2.61:180.23@2.9:191.96{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.29:24.6@0.58:48.76@0.87:71.93000000000001@1.16:93.67@1.45:113.64@1.74:131.63@2.03:147.49@2.32:161.19@2.61:172.77@2.9:182.37{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@1.04:84.73@1.3:102.7@1.56:118.85@1.82:132.87@2.08:144.62@2.34:154.32@2.6:162.63{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.78:63.95@1.04:82.48@1.3:99.17@1.56:113.77@1.82:126.03@2.08:135.81@2.34:143.08@2.6:147.98{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.48:39.82@0.72:57.88@0.96:74.73@1.2:90.05@1.44:103.44@1.68:114.52@1.92:123.17@2.16:129.6@2.4:134.53{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.24:19.02@0.48:37.18@0.72:54.09@0.96:69.39@1.2:82.77@1.44:94.01000000000001@1.68:102.98@1.92:109.68@2.16:114.25@2.4:116.99{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.25:18.84@0.5:36.05@0.75:51.39@1:64.56999999999999@1.25:75.36@1.5:83.61@1.75:89.38@2:92.95999999999999@2.25:94.95999999999999@2.5:96.40000000000001{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.39:20.38@0.78:35.33@1.17:46.14@1.56:53.84@1.95:59.2@2.34:62.84@2.73:65.23@3.12:66.75@3.51:67.76000000000001@3.9:68.59999999999999{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.5:14.7@1:25.11@1.5:32.41@2:37.55@2.5:41.26@3:44.07@3.5:46.33@4:48.28@4.5:50.02@5:51.59

Stress-strain (Cond.) -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.26:25.6@0.52:48.91@0.78:70.34@1.04:90.11@1.3:108.35@1.56:125.09@1.82:140.33@2.08:154.09@2.34:166.41@2.6:177.42{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.28:26.72@0.5600000000000001:51.24@0.84:73.47@1.12:93.48@1.4:111.42@1.68:127.41@1.96:141.47@2.24:153.42@2.52:162.82@2.8:168.85{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.25:23.69@0.5:45.59@0.75:65.48@1:83.34999999999999@1.25:99.28@1.5:113.36@1.75:125.58@2:135.75@2.25:143.39@2.5:147.63{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.23:21.22@0.46:40.81@0.6899999999999999:58.44@0.92:74.02@1.15:87.58@1.38:99.2@1.61:108.88@1.84:116.45@2.07:121.46@2.3:123.07{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.21:18.36@0.42:35.4@0.63:50.61@0.84:63.75@1.05:74.79000000000001@1.26:83.84999999999999@1.47:91.09@1.68:96.61@1.89:100.39@2.1:102.19{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.45:22.74@0.9:38.83@1.35:50.02@1.8:57.6@2.25:62.53@2.7:65.51000000000001@3.15:67.09999999999999@3.6:67.84@4.05:68.31999999999999@4.5:69.31{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.68:20.73@1.36:32.73@2.04:39.68@2.72:43.93@3.4:46.8@4.08:48.88@4.76:50.33@5.44:51.21@6.12:51.75@6.8:52.7

Secant modulus-strain -40|%|MPa|Strain in %|Secant modulus in MPa|0.29:8568.969999999999@0.58:8527.59@0.87:8413.790000000001@1.16:8242.24@1.45:8023.45@1.74:7769.54@2.03:7491.13@2.32:7199.14@2.61:6905.36@2.9:6619.31{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.29:8482.76@0.58:8406.9@0.87:8267.82@1.16:8075@1.45:7837.24@1.74:7564.94@2.03:7265.52@2.32:6947.84@2.61:6619.54@2.9:6288.62{n}0|%|MPa|Strain in %|Secant modulus in MPa|1.04:8147.12@1.3:7900@1.56:7618.59@1.82:7300.55@2.08:6952.88@2.34:6594.87@2.6:6255{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.78:8198.719999999999@1.04:7930.77@1.3:7628.46@1.56:7292.95@1.82:6924.73@2.08:6529.33@2.34:6114.53@2.6:5691.54{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.48:8295.83@0.72:8038.89@0.96:7784.38@1.2:7504.17@1.44:7183.33@1.68:6816.67@1.92:6415.1@2.16:6000@2.4:5605.42{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.24:7925@0.48:7745.83@0.72:7512.5@0.96:7228.12@1.2:6897.5@1.44:6528.47@1.68:6129.76@1.92:5712.5@2.16:5289.35@2.4:4874.58{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.25:7536@0.5:7210@0.75:6852@1:6457@1.25:6028.8@1.5:5574@1.75:5107.43@2:4648@2.25:4220.44@2.5:3856{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.39:5225.64@0.78:4529.49@1.17:3943.59@1.56:3451.28@1.95:3035.9@2.34:2685.47@2.73:2389.38@3.12:2139.42@3.51:1930.48@3.9:1758.97{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.5:2940@1:2511@1.5:2160.67@2:1877.5@2.5:1650.4@3:1469@3.5:1323.71@4:1207@4.5:1111.56@5:1031.8

Secant modulus-strain (Cond.) -40|%|MPa|Strain in %|Secant modulus in MPa|0.26:9846.15@0.52:9405.77@0.78:9017.950000000001@1.04:8664.42@1.3:8334.620000000001@1.56:8018.59@1.82:7710.44@2.08:7408.17@2.34:7111.54@2.6:6823.85{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.28:9542.860000000001@0.5600000000000001:9150@0.84:8746.43@1.12:8346.43@1.4:7958.57@1.68:7583.93@1.96:7217.86@2.24:6849.11@2.52:6461.11@2.8:6030.36{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.25:9476@0.5:9118@0.75:8730.67@1:8335@1.25:7942.4@1.5:7557.33@1.75:7176@2:6787.5@2.25:6372.89@2.5:5905.2{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.23:9226.09@0.46:8871.74@0.6899999999999999:8469.57@0.92:8045.65@1.15:7615.65@1.38:7188.41@1.61:6762.73@1.84:6328.8@2.07:5867.63@2.3:5350.87{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.21:8742.860000000001@0.42:8428.57@0.63:8033.33@0.84:7589.29@1.05:7122.86@1.26:6654.76@1.47:6196.6@1.68:5750.6@1.89:5311.64@2.1:4866.19{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.45:5053.33@0.9:4314.44@1.35:3705.19@1.8:3200@2.25:2779.11@2.7:2426.3@3.15:2130.16@3.6:1884.44@4.05:1686.91@4.5:1540.22{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.68:3048.53@1.36:2406.62@2.04:1945.1@2.72:1615.07@3.4:1376.47@4.08:1198.04@4.76:1057.35@5.44:941.36@6.12:845.588@6.8:775

Stress-strain (isochronous)(Creep) 23°C (cond.) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.09472999999999999:8@0.16607:14@0.23787:20@0.31033:26@0.38365:32@0.45804:38@0.53368:44@0.61078:50@0.68954:56{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.10004:8@0.17538:14@0.25135:20@0.32824:26@0.40635:32@0.48598:38@0.56741:44@0.6509200000000001:50@0.73678:56{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.10868:8@0.19046:14@0.27304:20@0.35689:26@0.44245:32@0.53016:38@0.62042:44@0.71362:50@0.81012:56{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.12275:8@0.21488:14@0.30796:20@0.40273:26@0.49987:32@0.60001:38@0.70373:44@0.81157:50@0.92401:56{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.14566:8@0.25441:14@0.36416:20@0.47607:26@0.59118:32@0.71043:38@0.83465:44@0.96458:50@1.10086:56{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.18299:8@0.31842:14@0.45461:20@0.5934:26@0.73639:32@0.88498:38@1.04038:44@1.20359:50@1.37548:56

Stress-strain (isochronous)(Creep) 120°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2567:6@0.345:8@0.4371:10@0.5354:12@0.6427:14@0.7625999999999999:16@0.8993:18@1.0576:20@1.2426:22@1.4599:24{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.2746:6@0.3686:8@0.4676:10@0.5747:12@0.6929999999999999:14@0.8259:16@0.9769:18@1.1494:20@1.3462:22@1.5699:24{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.3087:6@0.4114:8@0.5204:10@0.6393:12@0.7715:14@0.9199000000000001:16@1.0866:18@1.2728:20@1.4786:22@1.7036:24{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.3738:6@0.4892:8@0.6114000000000001:10@0.7454:12@0.8942:14@1.0597:16@1.2416:18@1.4385:20@1.6478:22@1.866:24{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.4983:6@0.6306:8@0.7688:10@0.9197:12@1.086:14@1.2673:16@1.4606:18@1.6613:20@1.864:22@2.0633:24

Creep modulus-time 23°C (cond.) 10|h|MPa|Time in h|Creep modulus in MPa|1:8440.93@10:7993.28@100:7358.99@1000:6518.18@10000:5497.34@100000:4381.44{n}20|h|MPa|Time in h|Creep modulus in MPa|1:8407.950000000001@10:7957.03@100:7324.93@1000:6494.35@10000:5492.09@100000:4399.38{n}30|h|MPa|Time in h|Creep modulus in MPa|1:8354.18@10:7891.42@100:7251.4@1000:6421.4@10000:5430.89@100000:4359.38{n}40|h|MPa|Time in h|Creep modulus in MPa|1:8279.709999999999@10:7798.55@100:7143.46@1000:6307.46@10000:5324.37@100000:4273.54{n}50|h|MPa|Time in h|Creep modulus in MPa|1:8186.25@10:7681.44@100:7006.53@1000:6160.9@10000:5183.6@100000:4154.24{n}56|h|MPa|Time in h|Creep modulus in MPa|1:8121.36@10:7600.64@100:6912.56@1000:6060.54@10000:5086.93@100000:4071.31

Creep modulus-time 120°C 5|h|MPa|Time in h|Creep modulus in MPa|10:2343.97@100:2189.39@1000:1940.57@10000:1589.42@100000:1174.99{n}10|h|MPa|Time in h|Creep modulus in MPa|10:2287.81@100:2138.58@1000:1921.6@10000:1635.59@100000:1300.73{n}15|h|MPa|Time in h|Creep modulus in MPa|10:2140.31@100:1980.42@1000:1778.24@10000:1538.7@100000:1276.68{n}20|h|MPa|Time in h|Creep modulus in MPa|10:1891.07@100:1740.04@1000:1571.34@10000:1390.34@100000:1203.88{n}24|h|MPa|Time in h|Creep modulus in MPa|10:1643.95@100:1528.76@1000:1408.78@10000:1286.17@100000:1163.19

Coefficient of Linear Thermal Expansion(CTE)-Temperature αn|°C|%|Temperature in °C|ΔL/L0 in %|-30:-0.34497@-20:-0.28254@-10:-0.21803@0:-0.15442@10:-0.08659@20:-0.02048@23:0@30:0.04502@40:0.11212@50:0.17993@55:0.21503@60:0.24849@70:0.32039@80:0.39813@90:0.4922@100:0.62832@110:0.8022@120:0.96962@130:1.11192@140:1.23865@150:1.36048@160:1.48617@170:1.61714@180:1.75471@190:1.90263@200:2.06195@210:2.2338@220:2.42265@230:2.62826@240:2.84362@250:3.05682@260:3.26337@270:3.47189@272:3.51856{n}αp|°C|%|Temperature in °C|ΔL/L0 in %|-30:-0.12213@-20:-0.10014@-10:-0.07718@0:-0.05482@10:-0.03137@20:-0.00739@23:0@30:0.01616@40:0.03987@50:0.06401999999999999@55:0.07618999999999999@60:0.08755@70:0.11179@80:0.13596@90:0.15918@100:0.18055@110:0.20011@120:0.21768@130:0.234@140:0.25003@150:0.26613@160:0.28308@170:0.30032@180:0.31819@190:0.33739@200:0.35822@210:0.38167@220:0.40775@230:0.43663@240:0.46816@250:0.49959@260:0.53081@270:0.56352@272:0.57137

Tensile modulus-temperature |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:8490@-20:8650@0:9240@23:8820@40:8920@60:8100@80:7540@100:4420@120:2720

Tensile modulus-temperature (cond.) |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:9215@-30:9098@-20:9114@-10:9067@0:8998@10:8851@20:8720@30:8587@40:8187@50:6025@60:4373@70:3427@80:2940

25% Glass Fiber